high temperature pipe sealing repair epoxy ceramic putty wearing compound coating

BD757 high temperature wearing resistant pipeline sealing repair epoxy ceramic bead putty compound
repairing,sealing and bonding of oil,water,steam,acid,alkali pipeline flange surface under various high
temperature working condition.


Xiangyang City Hundred Shield Coating Material Co.,Ltd



Company English Homepage: http://www.wearcoating.com

Tel:86-0710-3122805

Mobile:86-15072260980

CEO Email: jimmy@realbond.net

President Email: realbondsales@hotmail.com

Skype: changrongjimmy

Trademanager: wearcoatings


Product description of BD757 wearing high temperature resistant metal pipeline sealing repair epoxy
ceramic compound putty:

It’s the high temperature repairing agent consist of modified high temperature resin and high temperature curing agent,
it’s made of filling polymerization from ceramic,metal,fiber and so on,super-heated steam resistant,various acid & alkali 
corrosion resistant,oil resistant,good toughness,with a high bonding strength.
The touching temperature can reach to 300 degree,
can work under 250 degree for a long time.Suitable for the repairing,
sealing and bonding of oil,water,steam,acid,alkali pipeline flange 
surface under various high temperature working condition.

How to use of our BD757 high temperature metal pipeline repair sealing ceramic putty epoxy compound:

1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,
then clean it by cleaning agent.
 
2.Configuration: According to the mass ratio A:B=5:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,
and use it up within specified operation time limit.
 
3.Coating::Make the mixed-up material spread coating on the pending-repair area layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.

 
4.Curing:Cure for 24 hours at the normal temperature,or cure for 2 hours at the temperature of 25 degree,
then heat it up to the temperature of 80 degree and keep this temperature for 2 hours,if the temperature is low in winter,
can heat it up or prolong the curing time to complete the curing.

Product performance index:

product namephysical statestandard packagingVolume
(cm3)
operational time limit
(25℃)
curing time
(25℃)
757 high temperature sealing 
agent epoxy compound repair putty
paste500g/set
Two-component
36030min24h
colordensity
(g/cm3)
compressive strength
(kg/cm2)
GB1041-2008
shear strength
(kg/cm2)
GB7124-2008
bending strength
(kg/cm2)
GB1042-1999
hardness
(Shore D)
ASTM-D-2556
dielectric strength
(kv/mm)
working 
temperature
(℃)
gray1.48671201508616-60~300
 